Pulsed Laser Deposition of Granular Co-Ag Thin Films

E. Agostinelli, S. Alessandrini, D. Fiorani, A. Garcia Santiago, A.M. Testa, M. Angiolini, M. Vittori-Antisari

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

An investigation into the microstructural properties of CoxAg1 - xfilms, grown by pulsed laser deposition, as a function of deposition and post-deposition annealing temperature is reported. Surface morphology and microstructure were investigated by XPS, SEM and TEM measurements. Magnetic measurements were used to gain further information on particle size distributions through the analysis of the temperature dependence of the irreversible magnetization. Depending on cobalt content, deposition and post-deposition annealing temperature, the maximum of the cobalt grains diameter distribution was estimated to be in the range 2-6 nm. © 1998 John Wiley & Sons, Ltd.
Original languageEnglish
Pages (from-to)375 - 379
Number of pages5
JournalApplied Organometallic Chemistry
Volume12
Issue number5
DOIs
Publication statusPublished - 1998
Externally publishedYes

    Fingerprint

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Inorganic Chemistry

Cite this

Agostinelli, E., Alessandrini, S., Fiorani, D., Garcia Santiago, A., Testa, A. M., Angiolini, M., & Vittori-Antisari, M. (1998). Pulsed Laser Deposition of Granular Co-Ag Thin Films. Applied Organometallic Chemistry, 12(5), 375 - 379. https://doi.org/10.1002/(SICI)1099-0739(199805)12:5<375::AID-AOC733>3.0.CO;2-#